Top Level > Clear Heatshrink 2:1 Ratio
9.5mm Diameter Clear Heatshrink
£1.24
Clear Heatshrink 9.5mm Diameter x 1m
Supplied in 1 metre lengths
Shrink ratio 2:1
Shrinking temperature +80ºc
Made from polyolefin
Excellent flexibility and insulation
Excellent flame retardent properties
Temperature range -55°c to +125°c
UL approved
9.5mm is the internal diameter before shrinking
Purchase more than 1 length and it will be supplied in one continuous length
Weight per 1m length: 12grms
Heatshrink Measurements:
D = Diameter
F= Lay Flat Measurement
|
Inner Diameter mm
|
Wall Thickness As
Supplied mm
|
Wall Thickness After
Recovery mm
|
|
1.0mm
|
0.15 +/- 0.05
|
0.22 +/- 0.10
|
|
1.6mm
|
0.15 +/- 0.05
|
0.28 +/- 0.10
|
|
2.4mm
|
0.18 +/- 0.05
|
0.35 +/- 0.10
|
|
3.2mm
|
0.18 +/- 0.05
|
0.40 +/- 0.10
|
|
4.8mm
|
0.25 +/- 0.05
|
0.50 +/- 0.10
|
|
6.4mm
|
0.28 +/- 0.05
|
0.55 +/- 0.10
|
|
9.5mm
|
0.30 +/- 0.08
|
0.60 +/- 0.10
|
|
12.7mm
|
0.30 +/- 0.08
|
0.60 +/- 0.10
|
|
19.1mm
|
0.40 +/- 0.15
|
0.80 +/- 0.15
|
|
25.4mm
|
0.55 +/- 0.15
|
0.90 +/- 0.15
|
|
38.1mm
|
0.55 +/- 0.15
|
1.00 +/- 0.15
|
|
50.8mm
|
0.60 +/- 0.18
|
1.00 +/- 0.15
|
|
76mm
|
0.70 +/- 0.20
|
1.46 +/- 0.20
|
|
102mm
|
0.70 +/- 0.20
|
1.46 +/- 0.20
|
|
127mm
|
0.70 +/- 0.20
|
1.56 +/- 0.25
|
|
152mm
|
0.80 +/- 0.25
|
1.66 +/- 0.25
|
|
178mm
|
0.80 +/- 0.25
|
1.66 +/- 0.25
|
Technical Data
Property
Test Method
Typical Data
Tensile Strength
ASTM D 2671
14MPa
Ultimate Elongation (%)
ASTM D 2671
450
Longitudinal Shrinkage (%)
UL 224
+/- 5
Heat Aging
Tensile Strength
Ultimate Elongation (%)
158¡É,
168hr
11MPa
300
Flammability
UL224 VW-1
Pass
Heat shock (250¡É,
4hrs)
ASTM D 2671
No cracking
Cold bend tests (-55¡É,
4hrs)
ASTM D 2671
No cracking
Dielectric Strength (kv/mm)
ASTM D 150
20
Volume Resistivity (ohm-cm)
ASTM D 876
1x1014
Copper Stability
UL224
Pass